Exaton 309/309L
309/309L is suitable for joining stainless Cr-Ni steels of the 309 type, Cr-steels and dissimilar steels e.g. austenitic stainless steel to carbon or low-alloyed steels for service up to 320°C (610°F). It is used for MIG/MAG welding. Widely used as barrier layer between carbon/low alloy steel and different stainless grades in cladding operations.
Documents
Typical Tensile Properties
| Condition | Elongation | Tensile Strength | Yield Strength |
| As Welded | 32 % | 590 MPa (86 ksi) | 440 MPa (64 ksi) |
Recommended Welding Parameters
| Current | Voltage | Wire Diameter | Wire Feed Speed | |
| 40-120 A | 15-19 V | 0.8 mm (0.030 in.) | 4.0-8.0 m/min (157-315 in./min) | |
| 60-220 A | 15-28 V | 1.0 mm (0.040 in.) | 4.0-12.0 m/min (157-472 in./min) | |
| 150-260 A | 24-29 V | 1.2 mm (0.047 in.) | 3.0-10.0 m/min (118-394 in./min) | |
| 230-350 A | 25-30 V | 1.6 mm (1/16 in.) | 3.0-5.0 m/min (118-197 in./min) | |
Classifications
| Wire Electrode |
EN ISO 14343-A : G 23 12 L SFA/AWS A5.9 : ER309L Werkstoffnummer : 1.4332 |
Approvals
| Grade | EN 13479 |
| Society | CE |
| Approvals are based on factory location. Please contact ESAB for more information. |
Consumable Characteristics
| Alloy Type | Austenitic (with approx. 9 % ferrite) 24 % Cr - 13 % Ni - Low C |
Typical Weld Metal Analysis %
| Typical Weld Metal Analysis % | ||||||||||||||
| C | Co | Cr | Cu | FN WRC-92 | Mn | Mo | N | Nb | Ni | P | S | Si | V | |
| 0.01 % | 0.03 % | 23.6 % | 0.04 % | 12 % | 1.67 % | 0.01 % | 0.08 % | 0.01 % | 13.5 % | 0.018 % | 0.016 % | 0.40 % | 0.03 % | |
| Typical Wire Composition % | ||||||||||||||
| <0.02 % | - | 23.5 % | <0.1 % | 10 % | 1.8 % | <0.1 % | 0.08 % | - | 13.5 % | 0.01 % | 0.01 % | 0.4 % | - | |