Exaton NiCr-3

Exaton

Exaton NiCr-3

The following items have been added to your list


x

NiCr-3 is filler material for joining NiCrFe alloys, 9% Ni steels used at cryogenic temperatures, stainless steels to carbon steels, high service temperature NiCu alloys to carbon steels and NiCu alloys to nickel alloys. NiCr-3 can be used in air up to 1175°C (2145°F) and in sulphur dioxide atmospheres up to 800°C (1470°F). It is used for MIG/MAG welding.

BUY NOW


Exaton NiCr-3

Documents


Typical Tensile Properties

ConditionElongationTensile Strength Yield Strength
As Welded35 %660 MPa (96 ksi)420 MPa (61 ksi)

Recommended Welding Parameters

Current Voltage Wire Diameter Wire Feed Speed
40-120 A 15-19 V 0.8 mm (0.030 in.) 4.0-8.0 m/min (157-315 in./min)
60-220 A 15-28 V 1.0 mm (0.040 in.) 4.0-12.0 m/min (157-472 in./min)
150-260 A 24-29 V 1.2 mm (0.047 in.) 3.0-10.0 m/min (118-394 in./min)
230-350 A 25-30 V 1.6 mm (1/16 in.) 3.0-5.0 m/min (118-197 in./min)

Classifications

Wire Electrode SFA/AWS A5.14 : ERNiCr-3
EN ISO 18274 : S Ni 6082 (NiCr20Mn3Nb)

Approvals

Approvals CE EN 13479
VdTÜV 00073
Approvals are based on factory location. Please contact ESAB for more information.

Typical Weld Metal Analysis %

Typical Wire Composition %
Al C Co Cr Cu Fe Mn Mo N Nb Nb+Ta Ni P S Si Ti
0.4 % <=0.03 % <=0.1 % 20.0 % <=0.05 % <=1 % 3 % ≤0.05 % <=0.05 % 2.5 % 2.6 % 73 % <=0.01 % <=0.01 % 0.1 % 0.4 %
Typical Weld Metal Analysis %
- <0.02 % <0.02 % 20 % 0.01 % ≤1 % 3.2 % 0.01 % 0.03 % 2.2 % 2.5 % 73 % <0.003 % 0.003 % 0.01 % 0.4 %
x

Part Numbers and Accessories

Select All | Select None

Check box to add

Part Numbers : Exaton NiCr-3
S985082110 FIND A DISTRIBUTOR
S985089820 FIND A DISTRIBUTOR
S985103800 FIND A DISTRIBUTOR
S98510932H FIND A DISTRIBUTOR
S985109320 FIND A DISTRIBUTOR
S985109820 FIND A DISTRIBUTOR
S985129820 FIND A DISTRIBUTOR
S98512982H FIND A DISTRIBUTOR
S985129320 FIND A DISTRIBUTOR
S985169820 FIND A DISTRIBUTOR

ESAB EQUIPMENT WARRANTIES ARE VALID ONLY WHEN PURCHASED THROUGH AN ESAB AUTHORIZED DEALERSHIP.

x
x

x

Loading..