OK Autrod 317L

ESAB

OK Autrod 317L

The following items have been added to your list


x

A continuous, solid, corrosion-resistant, chromium-nickel-molybdenum wire for welding austenitic stainless alloys of the 19% Cr, 13% Ni, 3% Mo types. OK Autrod 317L has good resistance to general corrosion and pitting due to its high content of molybdenum. The alloy has a low carbon content which makes it particularly recommended where there is a risk of intergranular corrosion. The alloy is used in severe corrosion conditions, such as in the petrochemical, pulp and paper industries.

BUY NOW


Typical Charpy V-Notch Properties

Impact Value Testing Temperature
as welded
55 J (41 ft-lb) -196 degC (-321 degF)
135 J (100 ft-lb) 20 degC (68 degF)

Typical Tensile Properties

ConditionElongationTensile Strength Yield Strength
As Welded45 %600 MPa (87 ksi)390 MPa (57 ksi)

Deposition Data

Current Deposition Rate Diameter Voltage Wire Feed Speed
50-140 A 0.8-2.7 kg/h (1-6 lb/h) 0.8 mm (0.030 in.) 16-22 V 3.4-11.0 m/min (134-433 in./min)
180-280 A 2.6-4.5 kg/h (5-9 lb/h) 1.2 mm (0.047 in.) 20-28 V 4.9-8.5 m/min (193-335 in./min)
230-350 A 3.0-5.2 kg/h (6-11 lb/h) 1.6 mm (1/16 in.) 24-28 V 3.2-5.5 m/min (126-217 in./min)
80-190 A 0.9-2.7 kg/h (2-6 lb/h) 1.0 mm (0.040 in.) 16-24 V 2.6-7.1 m/min (102-280 in./min)

Classifications

Wire Electrode SFA/AWS A5.9 : ER317L
EN ISO 14343-A : G 18 15 3 L
Approvals are based on factory location. Please contact ESAB for more information.

Consumable Characteristics

Alloy Type Austenitic (with approx. 8 % ferrite)

Typical Weld Metal Analysis %

Typical Wire Composition %
C Cr FN WRC-92 Mn Mo N Ni Si
0.01 % 18.9 % 7 % 1.4 % 3.6 % 0.05 % 13.6 % 0.4 %
x

Part Numbers and Accessories

Select All | Select None

Check box to add

Part Numbers : OK Autrod 317L
1634089820 FIND A DISTRIBUTOR
1634109820 FIND A DISTRIBUTOR
1634129820 FIND A DISTRIBUTOR
1634240300 FIND A DISTRIBUTOR
1634320300 FIND A DISTRIBUTOR

ESAB EQUIPMENT WARRANTIES ARE VALID ONLY WHEN PURCHASED THROUGH AN ESAB AUTHORIZED DEALERSHIP.

x
x

x

Loading..