OK Autrod 316L
A continous solid corrosion resisting chromium-nickel-molybdenum wire for welding of austenitic stainless alloys of 18% Cr - 8% Ni and 18% Cr - 10% Ni - 3% Mo-types. OK Autrod 316L has a good general corrosion resistance, particularly against corrosion in acid and chlorinated environments. The alloy has a low carbon content which makes it particularly recommended were there is a risk of intergranular corrosion. The alloy is widely used in the chemical and food processing industries as well as in ship building and various types of architectural structures.
Typical Charpy V-Notch Properties
| Impact Value | Testing Temperature | |||
| as welded | ||||
| 55 J (40.5 ft-lb) | -196 degC (-321 degF) | |||
| 95 J (70 ft-lb) | -60 degC (-76 degF) | |||
| 120 J (88.5 ft-lb) | 20 degC (68 degF) | |||
| sht 1050°c (1922°f) 0.5h | ||||
| 50 J (67 ft-lb) | -196 degC (-321 degF) | |||
| 90 J (66 ft-lb) | -60 degC (-76 degF) | |||
| 110 J (81 ft-lb) | 20 degC (68 degF) | |||
Typical Tensile Properties
| Condition | As Welded | As Welded | SHT | SHT |
| 1050°C 0.5h | 1050°C 0.5h | |||
| Shielding Gas | Tested at 350°C. | Tested at 350°C. | ||
| Tensile Strength | 440 MPa | 620 MPa | 590 MPa | 430 MPa |
| Yield Strength | 340 MPa | 440 MPa | 350 MPa | 250 MPa |
| Elongation | 26 % | 37 % | 42 % | 31 % |
Deposition Data
| Current | Deposition Rate | Diameter | Voltage | Wire Feed Speed |
| 55-160 A | 1.0-4.1 kg/h (2-9 lb/h) | 0.8 mm (0.030 in.) | 15-24 V | 4.0-17.0 m/min (157-669 in./min) |
| 80-240 A | 1.5-6.0 kg/h (3-13 lb/h) | 1.0 mm (0.040 in.) | 15-28 V | 4.0-16.0 m/min (157-630 in./min) |
| 100-300 A | 1.6-7.5 kg/h (3-16 lb/h) | 1.2 mm (0.047 in.) | 15-29 V | 3.0-14.0 m/min (118-551 in./min) |
| 230-375 A | 5.2-8.6 kg/h (11-19 lb/h) | 1.6 mm (1/16 in.) | 23-31 V | 5.5-9.0 m/min (217-354 in./min) |
| 80-240 A | 1.5-6.0 kg/h (3-13 lb/h) | 1.14 mm (0.045 in.) | 15-28 V | 4.0-16.0 m/min (157-630 in./min) |
| 55-160 A | 1.0-4.1 kg/h (2-9 lb/h) | 0.9 mm (0.035 in.) | 15-24 V | 4.0-17.0 m/min (157-669 in./min) |
Classifications
| Wire Electrode |
Werkstoffnummer : ~1.4430 EN ISO 14343-A : G 19 12 3 L SFA/AWS A5.9 : ER316L |
Consumable Characteristics
| Alloy Type | Austenitic (with appr. 8 % ferrite) 19 % Cr - 12 % Ni - 3 % Mo - Low C |
Typical Weld Metal Analysis %
| Typical Wire Composition % | ||||||||||||||
| C | Cr | Cu | FN WRC-92 | Mn | Mo | N | Ni | P | S | Si | ||||
| 0.01 % | 18.2 % | - | 7 % | 1.7 % | 2.6 % | 0.04 % | 12.0 % | - | - | 0.4 % | ||||
| Typical Weld Metal Analysis % | ||||||||||||||
| 0.02 % | 18.5 % | 0.1 % | - | 1.8 % | 2.7 % | - | 12 % | 0.015 % | 0.015 % | 0.4 % | ||||