Stoody

Stoody HB-NoMag

Stoody HB-NoMag

Stoody HB-NoMag was designed to be a non-magnetic, crack free hardbanding alloy to be applied to non-magnetic down hole tooling and equipment. HB-NoMag produces a uniform distribution of small primary metal carbides in a fully austenitic chromium manganese matrix. Deposits are useful for rebuilding manganese, chrome-manganese and nitronic,non-magnetic stainless steel parts subject to severe impact loading combined with abrasion. HB-NoMag can be applied in multiple layers without spalling with proper welding procedures on austenitic manganese base metal.

Where To Buy


Features

  • Non-magnetic, crack free hardbanding of non-magnetic down hold tooling and equipment
  • Useful for rebuilding manganese, chrome-manganese and nitronic, non-magnetic stainless steel parts subject to severe impact loading combined with abrasion
  • Abrasion resistance three times superior to that of an austenitic manganese deposit as measured on the G65 test
  • Can be applied in multiple layers without spalling with proper welding procedures on austenitic manganese base metal


Specifications


Typical Tensile Properties

75% Ar - 25% CO2
Hardness (HRC)
50-53 HRC

Typical Weld Metal Analysis %

OtherMnCCrFe
5.5 %16.0 %2.0 %14.5 %BAL %

x

Typical Tensile Properties

75% Ar - 25% CO2
Hardness (HRC)
50-53 HRC

Typical Weld Metal Analysis %

OtherMnCCrFe
5.5 %16.0 %2.0 %14.5 %BAL %

x
x
×