Stoody 101AP open arc wire is a high chromium carbide iron base tubular wire. The higher chromium content aims at a minimum of 25% chromium (as well as a maximum of 0.18 g ASTM G65 weight loss) in a two layer weld deposit. Stoody 101AP was specially formulated to improve out of position horizontal welding when compared to other chrome carbide welding wires. The unique formulation is recommended for application subject to severe abrasion. The weld deposits develop a tight cross-checking pattern (3/8" - 1/2"). The cracking is sometimes referred to as relief cracking. It can be applied to carbon, low alloy or manganese steels and can be used in hot wear applications up to 900F (428C). Deposits cannot be machined or forged.

BUY NOW


Features

  • Abrasion Resistance: Excellent
  • Impact Resistance: Medium
  • Hardness, 2 layers on 1020 Carbon Steel, HRC: 60-64
  • Surface Cross Checks: Yes
  • Magnetic: Yes
  • Hot Wear Application: Up to 900F (482C)


Industries

  • Repair and Maintenance

Welding Process

  • GMAW (MIG/MAG)

Recommended Welding Parameters

Current TTW Dist. Voltage Wire Diameter
225-275 A 13-25 mm (1/2-1 in.) 24-28 V 1.6 mm (1/16 in.)
175-225 A 13-19 mm (1/2-3/4 in.) 23-27 V 1.2 mm (.045 in.)

Consumable Characteristics

Alloy Type Primary Chromium Carbides in an Austenitic Matrix