Shield-Bright 308H
Shield-Bright 308H was developed for welding Type 304H stainless steel and can also be used for welding Type 301, 302, and 304 steels. It contains a higher carbon level than 308L filler metals to give greater high temperature strength. The ferrite content is also lower for high temperature service. It has greater ductility than 347 types at high temperatures and for that reason it is sometimes used to weld Types 321 and 347 for service above 750°F (399°C) coupled with high stress.
Industries
- Industrial and General Fabrication
- Petrochemical
- Power Generation
Welding Process
- FCAW (Flux Core)
Typical Charpy V-Notch Properties
| Impact Value | Testing Temperature | |||
| as welded c1 shielding gas | ||||
| 26 J (19 ft-lb) | -196 degC (-321 degF) | |||
| 47 J (35 ft-lb) | -29 degC (-20 degF) | |||
| as welded c1 shielding gas | ||||
| 26 J (19 ft-lb) | -196 degC (-321 degF) | |||
| 47 J (35 ft-lb) | -29 degC (-20 degF) | |||
Typical Tensile Properties
| Elongation | Shielding Gas | Tensile Strength | Yield Strength |
| 46 % | M21 Shielding Gas | 580 MPa (84 ksi) | 371 MPa (54 ksi) |
Deposition Data
| Current | 130-220 A |
| Deposition Rate | 4.2-10.1 lb/h |
| Deposition Rate | 1.9-4.6 kg/h |
| Diameter | .045 in. |
| Diameter | 1.2 mm |
| Voltage | 24-29 V |
| Wire Feed Speed | 228-567 in./min |
| Wire Feed Speed | 5.8-14.4 m/min |
Classifications
| Weld Metal |
SFA/AWS A5.22 : E308HT1-1 SFA/AWS A5.22 : E308HT1-4 KS D 3612 : YF 308C EN ISO 17633-A : T 19 9 H P M21 2 JIS Z 3232 : TS308H-FB1 |
| Classifications |
EN ISO 17633-A : T 19 9 H P C1 2 |
| Weld Metal |
JIS Z 3323 : YF 308C |
Consumable Characteristics
| Alloy Type | C Cr Ni |
| Welding Current | DC+ |
Typical Weld Metal Analysis %
| Typical Weld Metal Analysis % | ||||||||||||||
| C | Cr | Mn | Ni | Si | ||||||||||
| 75% Ar - 25% CO2 | ||||||||||||||
| 0.05 % | 19.21 % | 1.08 % | 9.65 % | 0.87 % | ||||||||||
Part Numbers and Accessories