Dual Shield 88-C3

ESAB

Dual Shield 88-C3

The following items have been added to your list


x

Dual Shield 88-C3 is a 1% nickel flux cored wire developed for low temperature impact toughness. It is an excellent choice for welding weathering grade steel, such as Cor-Ten® where W grade electrodes are not desireable. Dual Shield 88-C3 wire is recommended for welding high strength steels in the 70-80 ksi (483-552 MPa) tensile range. The weld metal analysis is similar to an E8018-C3 low hydrogen electrode.

BUY NOW


Industries

  • Barges
  • Bridge Construction
  • Civil Construction
  • General Cast Iron Repair and Fabrication
  • Power Generation
  • Railcars
  • Ship/Barge Building

Welding Process

  • FCAW (Flux Core)

Typical Weld Metal Analysis %

Typical Weld Metal Analysis %
C Mn Ni P S Si
0.087 % 1.0 % 0.95 % 0.009 % 0.015 % 0.29 %

Approvals

Approvals MIL E-24403/1
MIL 80T1-Ni1C
Approvals are based on factory location. Please contact ESAB for more information.

Typical Charpy V-Notch Properties

Testing Temperature -29 degC
Testing Temperature -20 degF
Shielding Gas 100% CO2
Impact Value 49 J
Impact Value 36 ft-lb
As Welded

Classifications

ASME SFA 5.36 :
ASME SFA 5.29 :
AWS A5.36 : E80T1-C1A2-Ni1
AWS A5.29 : E80T1-Ni1C

Typical Tensile Properties

ConditionElongationReduction in AreaShielding GasTensile Strength Yield Strength
As Welded28 %60 %100% CO2593 MPa (86 ksi)517 MPa (75 ksi)

Deposition Data

Current Deposition Rate Diameter Efficiency (%) Voltage Wire Feed Speed
100% CO2
350 A 4.35 kg/h(9.6 lb/h) 2.4 mm(3/32 in.) 84 % 30 V 315 cm/min(124 in./min)
400 A 5.76 kg/h(12.7 lb/h) 2.4 mm(3/32 in.) 85 % 30 V 422 cm/min(166 in./min)
450 A 6.8 kg/h(15 lb/h) 2.4 mm(3/32 in.) 86 % 31 V 500 cm/min(197 in./min)
500 A 8.39 kg/h(18.5 lb/h) 2.4 mm(3/32 in.) 86 % 32 V 602 cm/min(237 in./min)
550 A 9.66 kg/h(21.3 lb/h) 2.4 mm(3/32 in.) 88 % 34 V 706 cm/min(278 in./min)