Dual Shield 8000-Ni2 is an all-position flux cored electrode that deposits 2.5% Ni deposit with an 82 ksi (565 MPa) minimum tensile strength. Dual Shield 8000-Ni2 may be used with CO2 or argon mixtures. The argon-CO2 mixtures reduce spatter and further improve weldability especially for small vertical-up fillets. Dual Shield 8000-Ni2 produces superior weld metal properties which make it most desirable for such applications as shipbuilding and heavy machinery construction. The weld metal analysis is similar to an E8018-C1 low hydrogen electrode.

BUY NOW


Industries

  • Bridge Construction
  • Industrial and General Fabrication
  • Mobile Equipment
  • Process

Welding Process

  • FCAW (Flux Core)

Typical Charpy V-Notch Properties

Impact Value Testing Temperature
as welded 100% co2
84 J (62 ft-lb) -18 degC (0 degF)
58 J (43 ft-lb) -29 degC (-20 degF)
53 J (39 ft-lb) -40 degC (-40 degF)
46 J (34 ft-lb) -51 degC (-60 degF)
as welded 75% ar - 25% co2
69 J (63 ft-lb) -18 degC (0 degF)
64 J (47 ft-lb) -29 degC (-20 degF)
54 J (40 ft-lb) -40 degC (-40 degF)
37 J (27 ft-lb) -51 degC (-60 degF)

Typical Tensile Properties

Condition As Welded As Welded
Reduction in Area 68 % 67 %
Shielding Gas 75% Ar - 25% CO2 100% CO2
Tensile Strength 620 MPa (90 ksi) 605 MPa (88 ksi)
Yield Strength 565 MPa (82 ksi) 550 MPa (80 ksi)
Elongation 27 % 26 %

Deposition Data

Current Deposition Rate Diameter Deposition Efficiency (%) TTW Dist. Voltage Wire Feed Speed
190 A 2.77 kg/h (6.1 lb/h) 1.6 mm (1/16 in.) 87 % 27 V 38 cm/min (150 in./min)
300 A 4.63 kg/h (10.2 lb/h) 1.6 mm (1/16 in.) 87 % 30 V 35 cm/min (250 in./min)
365 A 5.58 kg/h (12.3 lb/h) 1.6 mm (1/16 in.) 86 % 33 V 762 cm/min (300 in./min)
410 A 6.35 kg/h (14 lb/h) 1.6 mm (1/16 in.) 88 % 33 V 889 cm/min (350 in./min)
450 A 7.3 kg/h (16 lb/h) 1.6 mm (1/16 in.) 87 % 33 V 1016 cm/min (400 in./min)
500 A 9.11 kg/h (20.1 lb/h) 1.6 mm (1/16 in.) 87 % 39 V 1270 cm/min (500 in./min)
150 A 1.91 kg/h (4.2 lb/h) 1.2 mm (.045 in.) 86 % 28 V 508 cm/min (200 in./min)
210 A 86 kg/h (6.3 lb/h) 1.2 mm (.045 in.) 86 % 29 V 762 cm/min (300 in./min)
250 A 3.86 kg/h (8.5 lb/h) 1.2 mm (.045 in.) 87 % 30 V 1016 cm/min (400 in./min)
290 A 4.85 kg/h (10.7 lb/h) 1.2 mm (.045 in.) 87 % 33 V 1270 cm/min (500 in./min)
330 A 5.76 kg/h (12.7 lb/h) 1.2 mm (.045 in.) 87 % 34 V 1524 cm/min (600 in./min)
155 A 2 kg/h (4.4 lb/h) 1.4 mm (.052 in.) 87 % 25 V 381 cm/min (150 in./min)
245 A 3.31 kg/h (7.3 lb/h) 1.4 mm (.052 in.) 86 % 28 V 635 cm/min (250 in./min)
310 A 4.63 kg/h (10.2 lb/h) 1.4 mm (.052 in.) 85 % 33 V 889 cm/min (350 in./min)
360 A 6.03 kg/h (13.3 lb/h) 1.4 mm (.052 in.) 85 % 36 V 1143 cm/min (450 in./min)
430 A 7.98 kg/h (17.6 lb/h) 1.4 mm (.052 in.) 87 % 37 V 1524 cm/min (600 in./min)
100% CO2
315 A 1.6 mm (1/16 in.) 25 mm (1 in.) 32 V 699 mm/min (275 in./min)
305 A 1.6 mm (1/16 in.) 25 mm (1 in.) 28 V 640 mm/min (260 in./min)
200 A 1.6 mm (1/16 in.) 25 mm (1 in.) 24 V 381 mm/min (150 in./min)
190 A 1.2 mm (.045 in.) 19 mm (3/4 in.) 31 V 952 mm/min (375 in./min)
215 A 1.2 mm (.045 in.) 19 mm (3/4 in.) 28 V 914 mm/min (360 in./min)
140 A 1.2 mm (.045 in.) 19 mm (3/4 in.) 23 V 445 mm/min (175 in./min)
75% Ar - 25% CO2
315 A 1.6 mm (1/16 in.) 25 mm (1 in.) 32 V 699 mm/min (275 in./min)
305 A 1.6 mm (1/16 in.) 25 mm (1 in.) 27 V 640 mm/min (260 in./min)
200 A 1.6 mm (1/16 in.) 25 mm (1 in.) 24 V 381 mm/min (150 in./min)
225 A 1.2 mm (.045 in.) 19 mm (3/4 in.) 29 V 952 mm/min (375 in./min)
215 A 1.2 mm (.045 in.) 19 mm (3/4 in.) 27 V 914 mm/min (360 in./min)
140 A 1.2 mm (.045 in.) 19 mm (3/4 in.) 21 V 445 mm/min (175 in./min)

Classifications

Classifications AWS A5.29 : E81T1-Ni2C-JH8/E81T1-Ni2M H8
AWS A5.36 : E81T1-C1A6-Ni2-H8
AWS A5.36 : E81T1M21A4-Ni2-H8v

Approvals

Approvals A.B.S.- 3YSA
ASME SFA 5.29
AWS A5.29 E81T1-Ni2C/Ni2M
CERTIFIED BY C.W.B.- AWS A5.29
MIL-E-24403/1 MIL-81T1-Ni2C-J/Ni2M
Approvals are based on factory location. Please contact ESAB for more information.

Typical Weld Metal Analysis %

Typical Weld Metal Analysis %
C Mn Ni P S Si
100% CO2
0.05 % 0.90 % 2.20 % 0.012 % 0.010 % 0.30 %
75% Ar - 25% CO2
0.05 % 1.10 % 2.20 % 0.012 % 0.010 % 0.40 %
x

Part Numbers and Accessories

Select All | Select None

Check box to add

Part Numbers : Dual Shield 8000-NI2
245020409 FIND A DISTRIBUTOR
245020219 FIND A DISTRIBUTOR
245020383 FIND A DISTRIBUTOR

ESAB EQUIPMENT WARRANTIES ARE VALID ONLY WHEN PURCHASED THROUGH AN ESAB AUTHORIZED DEALERSHIP.

x
x

x

Loading..