OK Flux 10.72
Agglomerated aluminate-basic flux for Submerged Arc Welding especially for applications with toughness requirements at low temperature. Excellent slag removal also in narrow V-joints. For wind tower productions, pressure vessels, general constructions etc. Extremely high current carrying capacity. For single or multi wire procedures. Suitable for DC and AC welding. Single layer and multi layer welding of unlimited plate thickness.
Klasifikace
| Jakost | S A AB 1 57 AC H5 |
| Název | EN ISO 14174 |
Schválení
| Schválení |
CE EN 13479 DB 51.039.12 |
| Schválení jsou platná podle místa výroby. Prosím kontaktujte ESAB pro další informace. |
Charakteristika svařovacího materiálu
| Změna legování | No Silicon and moderately Manganese alloying |
| Index bazicity | nom: 1.9 |
| Hustota | nom: 1.2 kg/dm3 |
| Difuzní vodík | max 5 ml H/100g weld metal (Redried flux) |
| Velikost zrna | 0.315-2.0 mm (9x48 mesh) |
| Typ strusky | Aluminate-basic |
Spotřeba tavidla
| V | Hmotnost tavidla/1kg, drát DC | Hmotnost tavidla/1kg, drát AC |
| 26 V | 0.7 kg | 0.6 kg |
| 30 V | 1.0 kg | 0.9 kg |
| 34 V | 1.3 kg | 1.2 kg |
| 38 V | 1.6 kg | 1.4 kg |
| A | Rozměry | Rychlost přesunu |
| 580 A | Ø 4.0 mm | 55 cm/min |
Klasifikace
| Svařovací drát | AWS/EN | EN - po svaření | Po svaření | PWHT |
| OK Autrod 12.24 | A5.23:EA2/ 14171-A:S2Mo; 24598-A:S S Mo | 14171-A: S 46 3 AB S2Mo | A5.23: F8A5-EA2-A3 | A5.23: F8P5-EA2-A3 |
| OK Autrod 12.22 | A5.17:EM12K/ 14171-A:S2Si | 14171-A: S 38 5 AB S2Si | A5.17: F7A8-EM12K | A5.17: F6P8-EM12K |
| OK Autrod 13.27 | A5.23:ENi2/ 14171-A:S2Ni2 | 14171-A: S 46 6 AB S2Ni2 | A5.23: F8A8-ENi2-Ni2 | A5.23: F7P8-ENi2-Ni2 |
| OK Autrod 12.20 | A5.17:EM12/ 14171-A:S2 | 14171-A: S 38 5 AB S2 | A5.17: F7A8-EM12 | A5.17: F6P8-EM12 |
| OK Autrod 13.64 | A5.23:EA2TiB/ 14171-A:S2MoTiB | A5.23: F8TA8-EA2TiB | ||
| OK Autrod 13.62 | A5.23:EG/ 14171-A:SZ3TiB | - | ||
| OK Autrod 13.24 | A5.23:ENi6/ 14171-A:S3Ni1Mo0,2 | - |
Schválení
| Svařovací drát | CE | CWB | DB | DNV | GL | VdTÜV |
| OK Autrod 12.20 | * | - | * | - | - | * |
| OK Autrod 12.22 | * | * | * | * | * | * |
| OK Autrod 12.24 | * | - | * | - | - | * |
| OK Autrod 13.27 | * | - | - | - | - | - |
| *Pouze pro vybraný výrobní závod. Pro další informace prosím kontaktujte ESAB. Navštivte stránky esab.com a stáhněte si materiálový list konkrétní kombinaci tavidlo/drát kde jsou uvedeny potřebné detaily. |
Typické mechanické vlastnosti
| Svařovací drát | Podmínky | Mez skluzu | Mez pevnosti v tahu | Zkouška rázem | Prodloužení |
| OK Autrod 12.20 | Po svaření AWS DC+ | 415 MPa (60 ksi) |
500 MPa (73 ksi) |
125 J @ -30°C, (93 ft-lb @ -30 °F) 70 J @ -50°C, (52 ft-lb @ -50 °F) 50 J @ -62°C, (37 ft-lb @ -62 °F) 125 J @ -30°C, (93 ft-lb @ -22 °F) 100 J @ -40°C, (74 ft-lb @ -40 °F) 70 J @ -50°C, (52 ft-lb @ -58 °F) 50 J @ -62°C, (37 ft-lb @ -79.6 °F) |
30 % |
| OK Autrod 12.20 | Po svaření EN AC | 420 MPa | 500 MPa (73 ksi) |
140 J @ -30°C, (104 ft-lb @ -22 °F) 130 J @ -40°C, (96 ft-lb @ -40 °F) 80 J @ -50°C, (59 ft-lb @ -58 °F) |
33 % |
| OK Autrod 12.22 | Po svaření AWS DC+ | 415 MPa (60 ksi) |
500 MPa (73 ksi) |
120 J @ -30°C, (89 ft-lb @ -30 °F) 100 J @ -40°C, (74 ft-lb @ -40 °F) 70 J @ -50°C, (52 ft-lb @ -50 °F) 50 J @ -62°C, (37 ft-lb @ -62 °F) 120 J @ -30°C, (89 ft-lb @ -22 °F) 70 J @ -50°C, (52 ft-lb @ -58 °F) 50 J @ -62°C, (37 ft-lb @ -79.6 °F) |
30 % |
| OK Autrod 12.22 | Po svaření EN AC | 425 MPa | 500 MPa (73 ksi) |
140 J @ -30°C, (104 ft-lb @ -22 °F) 130 J @ -40°C, (96 ft-lb @ -40 °F) 80 J @ -50°C, (59 ft-lb @ -58 °F) |
32 % |
| OK Autrod 12.24 | Po svaření AWS DC+ | 500 MPa (73 ksi) |
590 MPa (86 ksi) |
60 J @ -30°C, (44 ft-lb @ -30 °F) 40 J @ -40°C, (30 ft-lb @ -40 °F) 35 J @ -46°C, (26 ft-lb @ -46 °F) 60 J @ -30°C, (44 ft-lb @ -22 °F) 35 J @ -46°C, (26 ft-lb @ -50.8 °F) |
25 % |
| OK Autrod 12.24 | Po svaření EN AC | 535 MPa | 600 MPa (87 ksi) |
70 J @ -30°C, (52 ft-lb @ -22 °F) 50 J @ -40°C, (37 ft-lb @ -40 °F) 40 J @ -50°C, (30 ft-lb @ -58 °F) |
24 % |
| OK Autrod 13.24 | Po svaření AWS DC+ | 530 MPa (77 ksi) |
660 MPa (96 ksi) |
90 J @ 0°C, (67 ft-lb @ 32 °F) 35 J @ -40°C, (26 ft-lb @ -40 °F) |
28 % |
| OK Autrod 13.27 | Po svaření AWS DC+ | 490 MPa (71 ksi) |
610 MPa (88 ksi) |
100 J @ -40°C, (74 ft-lb @ -40 °F) 80 J @ -51°C, (59 ft-lb @ -51 °F) 50 J @ -62°C, (37 ft-lb @ -62 °F) 80 J @ -51°C, (59 ft-lb @ -59.8 °F) 50 J @ -62°C, (37 ft-lb @ -79.6 °F) |
30 % |
| OK Autrod 13.27 | Po svaření EN AC | 520 MPa (75 ksi) |
610 MPa (88 ksi) |
120 J @ -30°C, (89 ft-lb @ -22 °F) 100 J @ -40°C, (74 ft-lb @ -40 °F) 80 J @ -50°C, (59 ft-lb @ -58 °F) 60 J @ -60°C, (44 ft-lb @ -76 °F) |
27 % |
| OK Autrod 13.62 | Po svaření (acc. AWS) Plate thickness: 12mm; Heat Input: 2.2kJ/mm; Side 1: 600A, 32V, 53cm/min; Side 2: 700A, 60cm/min; DC+ | 500 MPa (73 ksi) |
610 MPa (88 ksi) |
50 J @ -62°C, (37 ft-lb @ -62 °F) 50 J @ -62°C, (37 ft-lb @ -79.6 °F) |
27 % |
| OK Autrod 13.64 | Po svaření (acc. to AWS) Plate thickness 12mm Heat input 2.2kJ/mm 700A, 32V, 60cm/min DC+ | 560 MPa (81 ksi) |
660 MPa (96 ksi) |
50 J @ -62°C, (37 ft-lb @ -62 °F) 50 J @ -62°C, (37 ft-lb @ -79.6 °F) |
27 % |
Chemické složení svarového kovu
| Typického chemické složení svarového kovu v % | ||||||||||||||
| C | Mn | Mo | Ni | Si | ||||||||||
| OK Autrod 12.20 AC, 580A, 29V | ||||||||||||||
| 0.06 % | 1.4 % | - | - | 0.2 % | ||||||||||
| OK Autrod 12.20 DC+, 580A, 29V | ||||||||||||||
| 0.05 % | 1.5 % | - | - | 0.2 % | ||||||||||
| OK Autrod 12.22 AC, 580A, 29V | ||||||||||||||
| 0.06 % | 1.4 % | - | - | 0.3 % | ||||||||||
| OK Autrod 12.22 DC+, 580A, 29V | ||||||||||||||
| 0.05 % | 1.5 % | - | - | 0.3 % | ||||||||||
| OK Autrod 12.24 AC, 580A, 29V | ||||||||||||||
| 0.06 % | 1.5 % | 0.5 % | - | 0.2 % | ||||||||||
| OK Autrod 12.24 DC+, 580A, 29V | ||||||||||||||
| 0.05 % | 1.6 % | 0.5 % | - | 0.2 % | ||||||||||
| OK Autrod 13.27 AC, 580A, 29V | ||||||||||||||
| 0.07 % | 1.4 % | - | 2.2 % | 0.30 % | ||||||||||
| OK Autrod 13.27 DC+, 520A, 29V | ||||||||||||||
| 0.05 % | 1.4 % | - | 2.2 % | 0.30 % | ||||||||||