OK Flux 10.62
Agglomerated fluoride-basic flux for Submerged Arc Welding. Primarily for multi-run welding. For highest demands on impact properties, low temperature toughness, strength and CTOD-values. Especially suitable for narrow gap welding due to good slag detachability and smooth side-wall blending. For Offshore constructions, pressure vessels, power generation, shipbuilding, pipe mills, civil constructions, transport industries, etc. Produces low-oxygen weld metal (approx. 300 ppm) with hydrogen contents maximum 5 ml/100 g, in BlockPac (moisture protection) maximum 4 ml/100g. Operates optimally at the lower end of the voltage range. Designed for single and multi wire procedures, for butt and fillet welds. Works equally well on DC and AC current. Single layer and multi layer welding of unlimited plate thickness.
Svařovací proces
- SAW - Svařování pod tavidlem
Klasifikace
| Klasifikace |
EN ISO 14174 : S A FB 1 55 AC H5 EN ISO 14174 : S A FB 1 55 AC H4 only BlockPac/moisture-protection |
Schválení
| Schválení |
CE EN 13479 DB 51.039.07 PL : NAKS/HAKC RD 03-613-03 HG : NAKS/HAKC RD 03-613-03 |
| Schválení jsou platná podle místa výroby. Prosím kontaktujte ESAB pro další informace. |
Charakteristika svařovacího materiálu
| Změna legování | No Silicon or Manganese alloying |
| Index bazicity | nom: 3.2 |
| Hustota | nom: 1.1 kg/dm3 |
| Difuzní vodík | max 5 ml H/100g weld metal (Redried flux); max 4 ml H/100g in BlockPac (moisture protection) |
| Velikost zrna | 0.2-1.6 mm (10x65 mesh) |
| Typ strusky | Fluoride-basic |
Spotřeba tavidla
| V | Hmotnost tavidla/1kg, drát DC | Hmotnost tavidla/1kg, drát AC |
| 26 V | 0.7 kg | 0.6 kg |
| 30 V | 1.0 kg | 0.9 kg |
| 34 V | 1.3 kg | 1.2 kg |
| 38 V | 1.6 kg | 1.4 kg |
| A | Rozměry | Rychlost přesunu |
| 580 A | Ø 4.0 mm | 55 cm/min |
Klasifikace
| Svařovací drát | AWS/EN | EN - po svaření | Po svaření | PWHT |
| OK Autrod 12.32 | A5.17:EH12K/ 14171-A:S3Si | 14171-A: S 46 6 FB S3Si | A5.17: F7A8-EH12K | A5.17: F7P8-EH12K |
| OK Autrod 12.24 | A5.23:EA2/ 14171-A:S2Mo; 24598-A:S S Mo | 14171-A: S 46 4 FB S2Mo | A5.23: F8A6-EA2-A2 | A5.23: F8P6-EA2-A2 |
| OK Autrod 12.22 | A5.17:EM12K/ 14171-A:S2Si | 14171-A: S 38 5 FB S2Si | A5.17: F7A8-EM12K | A5.17: F6P8-EM12K |
| OK Autrod 12.34 | A5.23:EA4/ 14171-A:S3Mo; 24598-A:S S MnMo | 14171-A: S 50 4 FB S3Mo | A5.23: F8A6-EA4-A4 | A5.23: F8P6-EA4-A4 |
| OK Autrod 12.40 | A5.17:EH14/ 14171-A:S4 | 14171-A: S 50 4 FB S4 | A5.17: F7A6-EH14 | A5.17: F7P6-EH14 |
| OK Autrod 13.21 | A5.23:ENi1/ 14171-A:S2Ni1 | 14171-A: S 42 4 FB S2Ni1 | A5.23: F7A6-ENi1-Ni1 | A5.23: F7P8-ENi1-Ni1 |
| OK Autrod 13.27 | A5.23:ENi2/ 14171-A:S2Ni2 | 14171-A: S 46 7 FB S2Ni2 | A5.23: F7A10-ENi2-Ni2 | A5.23: F7P10-ENi2-Ni2 |
| OK Autrod 13.24 | A5.23:ENi6/ 14171-A:S3Ni1Mo0,2 | 14171-A: S 50 6 FB S3Ni1Mo0.2 | A5.23: F8A10-ENi6-Ni6 | A5.23: F8P8-ENi6-Ni6 |
| OK Autrod 13.43 | A5.23:EG/ 26304-A:S3Ni2,5CrMo; 26304-B:(SUN4C1M3) | 26304-A: S 69 6 FB S3Ni2,5CrMo | A5.23: F11A8-EG-G | A5.23: F11P8-EG-G |
| OK Autrod 13.40 | A5.23:EG/ 14171-A:S3Ni1Mo; 26304-A:S3Ni1Mo; 26304-B:(SUN2M2) | 26304-A: S 62 6 FB S3Ni1Mo (AC) | A5.23: F10A8-EG-F3 (AC) | A5.23: F9P8-EG-F3 |
| OK Autrod 13.49 | A5.23:ENi3/ 14171-A:S2Ni3 | 14171-A: S 46 8 FB S2Ni3 | A5.23: F8A15-ENi3-Ni3 | A5.23: F8P15-ENi3-Ni3 |
| OK Autrod 13.10 SC | A5.23:EB2R/ 24598-A:S S CrMo1 | - | A5.23: F8P2-EB2R-B2 | |
| OK Autrod 12.44 | A5.23:EA3/ 24598-B:SU 4M3 | A5.23: F9A8-EA3-A3 | A5.23: F9P8-EA3-A3 | |
| OK Autrod 13.20 SC | A5.23:EB3R/ 24598-A:S S CrMo2 | - | A5.23: F8P2-EB3R-B3 | |
| OK Autrod 13.44 | A5.23:EG/ 26304-A:S3Ni1,5CrMo | 26304-A: S 62 5 FB S3Ni1,5CrMo | A5.23: F9A8-EG-G | |
| OK Autrod 12.40L India | A5.17:EH14 | A5.17: F7A6-EH14 | A5.17: F7P6-EH14 | |
| ESAB SA10K | A5.17:EH10K | A5.17: F7A6-EH10K | A5.17: F7P8-EH10K | |
| OK Autrod 12.24L | A5.23:EA2/ 14171-B:SU2M3 | A5.23: F8A4-EA2-A2 | A5.23: F8P4-EA2-A2 | |
| OK Autrod 12.40L | A5.17:EH14/ 14171-B:SU41 | A5.17: F7A6-EH14 | A5.17: F7P6-EH14 | |
| OK Autrod 12.33L | A5.23:EA3K | A5.23: F10A4-EA3K-G | A5.23: F9P4-EA3K-G | |
| OK Autrod 13.36 | A5.23:EG/ 14171-A:S2Ni1Cu | 14171-A: S 46 5 FB S2Ni1Cu | A5.23: F8A6-EG-G |
Schválení
| Svařovací drát | ABS | BV | CE | DB | DNV | DNV-GL | GL | LR | RINA | RS | VdTÜV |
| OK Autrod 12.22 | * | * | * | * | * | - | * | * | - | - | * |
| OK Autrod 12.24 | - | - | * | - | - | - | - | - | - | - | * |
| OK Autrod 12.32 | * | * | * | * | * | - | * | * | * | * | * |
| OK Autrod 12.34 | * | * | - | - | * | - | * | * | - | * | - |
| OK Autrod 12.40 | - | - | - | - | - | * | - | - | - | - | - |
| OK Autrod 13.10 SC | - | - | * | * | - | - | - | - | - | - | * |
| OK Autrod 13.20 SC | - | - | * | - | - | - | - | - | - | - | * |
| OK Autrod 13.24 | * | * | * | - | * | - | * | * | - | - | - |
| OK Autrod 13.27 | * | * | * | * | * | - | * | * | * | * | * |
| OK Autrod 13.36 | - | - | * | - | - | - | - | - | - | - | - |
| OK Autrod 13.40 | * | * | * | - | * | - | * | * | - | - | * |
| OK Autrod 13.43 | * | * | * | - | * | - | * | * | - | - | - |
| OK Tubrod 15.27S | * | - | * | - | * | - | * | * | - | - | - |
| *Pouze pro vybraný výrobní závod. Pro další informace prosím kontaktujte ESAB. Navštivte stránky esab.com a stáhněte si materiálový list konkrétní kombinaci tavidlo/drát kde jsou uvedeny potřebné detaily. |
Typické mechanické vlastnosti
| Svařovací drát | Podmínky | Mez skluzu | Mez pevnosti v tahu | Zkouška rázem | Prodloužení | Doba testu |
| ESAB SA10K | PWHT DC+ | 450 MPa (65 ksi),410 MPa (59 ksi) |
540 MPa (78 ksi),520 MPa (75 ksi),510 MPa (74 ksi) |
110 J @ -29°C, (81 ft-lb @ -20.2 °F) 80 J @ -40°C, (59 ft-lb @ -40 °F) 35 J @ -51°C, (26 ft-lb @ -59.8 °F) 30 J @ -62°C, (22 ft-lb @ -79.6 °F) 200 J @ -40°C, (148 ft-lb @ -40 °F) 140 J @ -51°C, (104 ft-lb @ -59.8 °F) 40 J @ -62°C, (30 ft-lb @ -79.6 °F) 230 J @ -40°C, (170 ft-lb @ -40 °F) 170 J @ -51°C, (126 ft-lb @ -59.8 °F) 100 J @ -62°C, (74 ft-lb @ -79.6 °F) 210 J @ -40°C, (155 ft-lb @ -40 °F) 180 J @ -51°C, (133 ft-lb @ -59.8 °F) 105 J @ -62°C, (78 ft-lb @ -79.6 °F) |
30 %,35 %,36 %,37 % | 1 hr,5 hr,10 hr,15 hr |
| ESAB SA10K | Po svaření DC+ | 490 MPa (71 ksi) |
570 MPa (83 ksi) |
100 J @ -29°C, (74 ft-lb @ -20.2 °F) 55 J @ -40°C, (41 ft-lb @ -40 °F) 40 J @ -51°C, (30 ft-lb @ -59.8 °F) |
28 % | |
| OK Autrod 12.22 | Po svaření AWS DC+ | 410 MPa (59 ksi) |
500 MPa (73 ksi) |
170 J @ 0°C, (126 ft-lb @ 32 °F) 160 J @ -20°C, (118 ft-lb @ -4 °F) 90 J @ -40°C, (67 ft-lb @ -40 °F) 70 J @ -50°C, (52 ft-lb @ -58 °F) 35 J @ -62°C, (26 ft-lb @ -79.6 °F) |
33 % | |
| OK Autrod 12.22 | Po svaření EN AC | 440 MPa | 510 MPa (74 ksi) |
180 J @ 0°C, (133 ft-lb @ 32 °F) 170 J @ -20°C, (126 ft-lb @ -4 °F) 90 J @ -40°C, (67 ft-lb @ -40 °F) 80 J @ -50°C, (59 ft-lb @ -58 °F) |
29 % | |
| OK Autrod 12.24 | Po svaření AWS DC+ | 500 MPa (73 ksi) |
580 MPa (84 ksi) |
140 J @ 20°C, (104 ft-lb @ 68 °F) 115 J @ 0°C, (85 ft-lb @ 32 °F) 80 J @ -20°C, (59 ft-lb @ -4 °F) 60 J @ -40°C, (44 ft-lb @ -40 °F) 45 J @ -51°C, (33 ft-lb @ -59.8 °F) |
25 % | |
| OK Autrod 12.24 | Po svaření EN AC | 520 MPa | 600 MPa (87 ksi) |
150 J @ 20°C, (111 ft-lb @ 68 °F) 125 J @ 0°C, (93 ft-lb @ 32 °F) 100 J @ -20°C, (74 ft-lb @ -4 °F) 55 J @ -40°C, (41 ft-lb @ -40 °F) 40 J @ -51°C, (30 ft-lb @ -59.8 °F) |
24 % | |
| OK Autrod 12.24L | PWHT DC+ | 530 MPa (77 ksi) |
590 MPa (86 ksi) |
70 J @ -18°C, (52 ft-lb @ -0.4 °F) 35 J @ -29°C, (26 ft-lb @ -20.2 °F) 30 J @ -40°C, (22 ft-lb @ -40 °F) |
27 % | 1 hr |
| OK Autrod 12.24L | Po svaření DC+ | 550 MPa (80 ksi) |
620 MPa (90 ksi) |
90 J @ -18°C, (67 ft-lb @ -0.4 °F) 40 J @ -29°C, (30 ft-lb @ -20.2 °F) 30 J @ -40°C, (22 ft-lb @ -40 °F) |
25 % | |
| OK Autrod 12.32 | Po svaření AWS DC+ | 475 MPa (69 ksi) |
560 MPa (81 ksi) |
175 J @ 20°C, (130 ft-lb @ 68 °F) 150 J @ 0°C, (111 ft-lb @ 32 °F) 130 J @ -30°C, (96 ft-lb @ -22 °F) 110 J @ -40°C, (81 ft-lb @ -40 °F) 70 J @ -62°C, (52 ft-lb @ -79.6 °F) |
28 % | |
| OK Autrod 12.32 | Po svaření EN AC | 520 MPa | 600 MPa (87 ksi) |
175 J @ 20°C, (130 ft-lb @ 68 °F) 170 J @ 0°C, (126 ft-lb @ 32 °F) 110 J @ -30°C, (81 ft-lb @ -22 °F) 90 J @ -40°C, (67 ft-lb @ -40 °F) 60 J @ -60°C, (44 ft-lb @ -76 °F) |
26 % | |
| OK Autrod 12.33L | PWHT DC+ | 620 MPa (90 ksi) |
690 MPa (100 ksi) |
50 J @ -29°C, (37 ft-lb @ -20.2 °F) 30 J @ -40°C, (22 ft-lb @ -40 °F) |
26 % | 1 hr |
| OK Autrod 12.33L | Po svaření DC+ | 660 MPa (96 ksi) |
740 MPa (107 ksi) |
45 J @ -29°C, (33 ft-lb @ -20.2 °F) 30 J @ -40°C, (22 ft-lb @ -40 °F) |
25 % | |
| OK Autrod 12.34 | Po svaření AWS DC+ | 540 MPa (78 ksi) |
620 MPa (90 ksi) |
170 J @ 20°C, (126 ft-lb @ 68 °F) 160 J @ 0°C, (118 ft-lb @ 32 °F) 140 J @ -20°C, (104 ft-lb @ -4 °F) 115 J @ -40°C, (85 ft-lb @ -40 °F) 45 J @ -51°C, (33 ft-lb @ -59.8 °F) |
24 % | |
| OK Autrod 12.34 | Po svaření EN AC | 560 MPa | 630 MPa (91 ksi) |
160 J @ 20°C, (118 ft-lb @ 68 °F) 150 J @ 0°C, (111 ft-lb @ 32 °F) 130 J @ -20°C, (96 ft-lb @ -4 °F) 100 J @ -40°C, (74 ft-lb @ -40 °F) 55 J @ -51°C, (41 ft-lb @ -59.8 °F) |
25 % | |
| OK Autrod 12.40 | Po svaření AWS DC+ | 530 MPa (77 ksi) |
620 MPa (90 ksi) |
140 J @ 20°C, (104 ft-lb @ 68 °F) 110 J @ 0°C, (81 ft-lb @ 32 °F) 80 J @ -20°C, (59 ft-lb @ -4 °F) 50 J @ -40°C, (37 ft-lb @ -40 °F) 40 J @ -51°C, (30 ft-lb @ -59.8 °F) |
26 % | |
| OK Autrod 12.40 | Po svaření EN AC | 550 MPa | 630 MPa (91 ksi) |
150 J @ 20°C, (111 ft-lb @ 68 °F) 105 J @ 0°C, (78 ft-lb @ 32 °F) 70 J @ -20°C, (52 ft-lb @ -4 °F) 55 J @ -40°C, (41 ft-lb @ -40 °F) 40 J @ -51°C, (30 ft-lb @ -59.8 °F) |
22 % | |
| OK Autrod 12.40L | PWHT DC+ | 450 MPa (65 ksi) |
550 MPa (80 ksi) |
110 J @ -29°C, (81 ft-lb @ -20.2 °F) 90 J @ -40°C, (67 ft-lb @ -40 °F) 50 J @ -51°C, (37 ft-lb @ -59.8 °F) |
28 % | 1 hr |
| OK Autrod 12.40L | Po svaření DC+ | 520 MPa (75 ksi) |
610 MPa (88 ksi) |
100 J @ -29°C, (74 ft-lb @ -20.2 °F) 85 J @ -40°C, (63 ft-lb @ -40 °F) 40 J @ -51°C, (30 ft-lb @ -59.8 °F) |
26 % | |
| OK Autrod 12.44 | Po svaření AWS DC+ | 600 MPa | 700 MPa | 105 J 80 J 65 J 50 J |
27 % | |
| OK Autrod 13.21 | Po svaření AWS DC+ | 470 MPa (68 ksi) |
560 MPa (81 ksi) |
195 J @ 20°C, (144 ft-lb @ 68 °F) 185 J @ 0°C, (137 ft-lb @ 32 °F) 160 J @ -20°C, (118 ft-lb @ -4 °F) 70 J @ -40°C, (52 ft-lb @ -40 °F) 60 J @ -51°C, (44 ft-lb @ -59.8 °F) |
28 % | |
| OK Autrod 13.21 | Po svaření EN AC | 520 MPa | 595 MPa (86 ksi) |
170 J @ 20°C, (126 ft-lb @ 68 °F) 165 J @ 0°C, (122 ft-lb @ 32 °F) 150 J @ -20°C, (111 ft-lb @ -4 °F) 70 J @ -40°C, (52 ft-lb @ -40 °F) 50 J @ -51°C, (37 ft-lb @ -59.8 °F) |
24 % | |
| OK Autrod 13.24 | Po svaření AWS DC+ | 530 MPa (77 ksi) |
620 MPa (90 ksi) |
120 J @ -40°C, (89 ft-lb @ -40 °F) 110 J @ -50°C, (81 ft-lb @ -58 °F) 70 J @ -60°C, (52 ft-lb @ -76 °F) 50 J @ -73°C, (37 ft-lb @ -99.4 °F) |
25 % | |
| OK Autrod 13.24 | Po svaření EN AC | 560 MPa | 640 MPa (93 ksi) |
130 J @ -40°C, (96 ft-lb @ -40 °F) 120 J @ -50°C, (89 ft-lb @ -58 °F) 80 J @ -60°C, (59 ft-lb @ -76 °F) |
23 % | |
| OK Autrod 13.27 | Po svaření AWS DC+ | 460 MPa (67 ksi) |
570 MPa (83 ksi) |
140 J @ -20°C, (104 ft-lb @ -4 °F) 110 J @ -40°C, (81 ft-lb @ -40 °F) 80 J @ -60°C, (59 ft-lb @ -76 °F) 50 J @ -73°C, (37 ft-lb @ -99.4 °F) |
28 % | |
| OK Autrod 13.27 | Po svaření EN AC | 520 MPa | 605 MPa (88 ksi) |
150 J @ -20°C, (111 ft-lb @ -4 °F) 120 J @ -40°C, (89 ft-lb @ -40 °F) 80 J @ -60°C, (59 ft-lb @ -76 °F) 60 J @ -70°C, (44 ft-lb @ -94 °F) |
27 % | |
| OK Autrod 13.36 | Po svaření AWS DC+ | 500 MPa (73 ksi) |
590 MPa (86 ksi) |
70 J @ -40°C, (52 ft-lb @ -40 °F) 60 J @ -51°C, (44 ft-lb @ -59.8 °F) |
27 % | |
| OK Autrod 13.36 | Po svaření EN AC | 550 MPa | 620 MPa (90 ksi) |
110 J @ -40°C, (81 ft-lb @ -40 °F) 90 J @ -50°C, (67 ft-lb @ -58 °F) |
25 % | |
| OK Autrod 13.40 | Po svaření AWS AC | 650 MPa (94 ksi) |
730 MPa (106 ksi) |
100 J @ -40°C, (74 ft-lb @ -40 °F) 90 J @ -50°C, (67 ft-lb @ -58 °F) 60 J @ -62°C, (44 ft-lb @ -79.6 °F) |
23 % | |
| OK Autrod 13.40 | Po svaření AWS DC+ | 610 MPa (88 ksi) |
690 MPa (100 ksi) |
90 J @ -40°C, (67 ft-lb @ -40 °F) 80 J @ -50°C, (59 ft-lb @ -58 °F) 50 J @ -62°C, (37 ft-lb @ -79.6 °F) |
24 % | |
| OK Autrod 13.40 | Po svaření EN AC | 660 MPa (96 ksi) |
730 MPa (106 ksi) |
110 J @ -40°C, (81 ft-lb @ -40 °F) 90 J @ -50°C, (67 ft-lb @ -58 °F) 70 J @ -60°C, (52 ft-lb @ -76 °F) |
24 % | |
| OK Autrod 13.40 | Po svaření EN DC+ | 620 MPa (90 ksi) |
700 MPa (102 ksi) |
100 J @ -40°C, (74 ft-lb @ -40 °F) 80 J @ -50°C, (59 ft-lb @ -58 °F) 60 J @ -60°C, (44 ft-lb @ -76 °F) 50 J @ -62°C, (37 ft-lb @ -79.6 °F) |
23 % | |
| OK Autrod 13.43 | Po svaření AWS DC+ | 700 MPa (102 ksi) |
800 MPa (116 ksi) |
100 J @ -20°C, (74 ft-lb @ -4 °F) 75 J @ -40°C, (56 ft-lb @ -40 °F) 65 J @ -50°C, (48 ft-lb @ -58 °F) 50 J @ -62°C, (37 ft-lb @ -79.6 °F) |
21 % | |
| OK Autrod 13.43 | Po svaření EN ISO-A AC | 720 MPa (104 ksi) |
845 MPa (123 ksi) |
110 J @ -20°C, (81 ft-lb @ -4 °F) 90 J @ -40°C, (67 ft-lb @ -40 °F) 70 J @ -50°C, (52 ft-lb @ -58 °F) 60 J @ -60°C, (44 ft-lb @ -76 °F) |
19 % | |
| OK Autrod 13.44 | Po svaření AWS DC+ | 610 MPa | 700 MPa | 95 J 80 J 55 J 40 J |
22 % | |
| OK Autrod 13.49 | Po svaření AWS DC+ | 500 MPa (73 ksi) |
600 MPa (87 ksi) |
95 J @ -70°C, (70 ft-lb @ -94 °F) 40 J @ -101°C, (30 ft-lb @ -149.8 °F) |
27 % | |
| OK Autrod 13.49 | Po svaření EN AC | 560 MPa | 640 MPa (93 ksi) |
95 J @ -70°C, (70 ft-lb @ -94 °F) 75 J @ -80°C, (56 ft-lb @ -112 °F) 55 J @ -90°C, (41 ft-lb @ -130 °F) |
22 % |
Chemické složení svarového kovu
| Typického chemické složení svarového kovu v % | ||||||||||||||
| C | Cr | Cu | Mn | Mo | Ni | P | S | Si | ||||||
| ESAB SA10K DC+ 550A, 29V | ||||||||||||||
| 0.08 % | - | - | 1.45 % | - | - | - | - | 0.25 % | ||||||
| OK Autrod 12.22 AC, 580 A, 29 V | ||||||||||||||
| 0.10 % | - | - | 0.95 % | - | - | - | - | 0.27 % | ||||||
| OK Autrod 12.22 DC+, 580 A, 29 V | ||||||||||||||
| 0.07 % | - | - | 1.0 % | - | - | - | - | 0.30 % | ||||||
| OK Autrod 12.24 DC+, 580A, 29V | ||||||||||||||
| 0.07 % | - | - | 1.0 % | 0.5 % | - | - | - | 0.22 % | ||||||
| OK Autrod 12.24L DC+ 550A, 29V | ||||||||||||||
| 0.07 % | - | - | 1.10 % | 0.45 % | - | 0.025 % | 0.015 % | 0.25 % | ||||||
| OK Autrod 12.32 AC, 580A, 29V | ||||||||||||||
| 0.11 % | - | - | 1.5 % | - | - | - | - | 0.3 % | ||||||
| OK Autrod 12.32 DC+, 580A, 29V | ||||||||||||||
| 0.10 % | - | - | 1.6 % | - | - | - | - | 0.35 % | ||||||
| OK Autrod 12.33L | ||||||||||||||
| 0.06 % | - | - | 1.70 % | 0.40 % | - | - | - | 0.75 % | ||||||
| OK Autrod 12.34 AC, 580A, 29V | ||||||||||||||
| 0.13 % | - | - | 1.4 % | 0.5 % | - | - | - | 0.18 % | ||||||
| OK Autrod 12.34 DC+, 580A, 29V | ||||||||||||||
| 0.10 % | - | - | 1.45 % | 0.5 % | - | - | - | 0.21 % | ||||||
| OK Autrod 12.40 AC, 580A, 29V | ||||||||||||||
| 0.12 % | - | - | 1.85 % | - | - | - | - | 0.10 % | ||||||
| OK Autrod 12.40 DC+, 580A, 29V | ||||||||||||||
| 0.08 % | - | - | 1.9 % | - | - | - | - | 0.12 % | ||||||
| OK Autrod 12.40L DC+ 550A, 29V | ||||||||||||||
| 0.09 % | - | - | 1.75 % | - | - | - | - | 0.15 % | ||||||
| OK Autrod 13.10 SC AC, 580A, 29V | ||||||||||||||
| 0.10 % | 1.1 % | - | 0.7 % | 0.5 % | - | - | - | 0.20 % | ||||||
| OK Autrod 13.10 SC DC+, 580A, 29V | ||||||||||||||
| 0.08 % | 1.1 % | - | 0.7 % | 0.5 % | - | - | - | 0.22 % | ||||||
| OK Autrod 13.20 SC AC, 580A, 29V | ||||||||||||||
| 0.09 % | 2.2 % | - | 0.60 % | 1.0 % | - | - | - | 0.20 % | ||||||
| OK Autrod 13.20 SC DC+, 580A, 29V | ||||||||||||||
| 0.08 % | 2.2 % | - | 0.60 % | 0.95 % | - | - | - | 0.20 % | ||||||
| OK Autrod 13.21 AC, 580A, 29V | ||||||||||||||
| 0.08 % | - | - | 0.95 % | - | 0.9 % | - | - | 0.22 % | ||||||
| OK Autrod 13.21 DC+, 580A, 29V | ||||||||||||||
| 0.06 % | - | - | 1.0 % | - | 0.9 % | - | - | 0.25 % | ||||||
| OK Autrod 13.24 AC, 580A, 29V | ||||||||||||||
| 0.10 % | - | - | 1.3 % | 0.2 % | 0.9 % | - | - | 0.25 % | ||||||
| OK Autrod 13.24 DC+, 580A, 29V | ||||||||||||||
| 0.08 % | - | - | 1.4 % | 0.2 % | 0.9 % | - | - | 0.30 % | ||||||
| OK Autrod 13.27 AC, 580A, 29V | ||||||||||||||
| 0.08 % | - | - | 0.95 % | - | 2.1 % | - | - | 0.22 % | ||||||
| OK Autrod 13.27 DC+, 580A, 29V | ||||||||||||||
| 0.06 % | - | - | 1.0 % | - | 2.1 % | - | - | 0.25 % | ||||||
| OK Autrod 13.36 AC, 580A, 29V | ||||||||||||||
| 0.10 % | 3 % | 0.4 % | 0.9 % | - | 0.7 % | - | - | 0.3 % | ||||||
| OK Autrod 13.36 DC+, 525A, 29V | ||||||||||||||
| 0.08 % | 0.3 % | 0.4 % | 1.0 % | - | 0.7 % | - | - | 0.3 % | ||||||
| OK Autrod 13.40 AC, 580A, 29V | ||||||||||||||
| 0.10 % | - | - | 1.45 % | 0.5 % | 0.9 % | - | - | 0.23 % | ||||||
| OK Autrod 13.40 DC+, 580A, 29V | ||||||||||||||
| 0.07 % | - | - | 1.50 % | 0.5 % | 0.9 % | - | - | 0.26 % | ||||||
| OK Autrod 13.43 AC, 580A, 29V | ||||||||||||||
| 0.12 % | 0.6 % | - | 1.45 % | 0.5 % | 2.2 % | - | - | 0.22 % | ||||||
| OK Autrod 13.43 DC+, 580A, 29V | ||||||||||||||
| 0.11 % | 0.6 % | - | 1.5 % | 0.5 % | 2.2 % | - | - | 0.25 % | ||||||
| OK Autrod 13.49 AC, 580A, 29V | ||||||||||||||
| 0.08 % | - | - | 0.95 % | - | 3.1 % | - | - | 0.20 % | ||||||
| OK Autrod 13.49 DC+, 580A, 29V | ||||||||||||||
| 0.06 % | - | - | 1.0 % | - | 3.1 % | - | - | 0.25 % | ||||||