Exaton 10SW
Exaton 10SW is a chromium-compensating agglomerated flux giving good slag removal and a fine bead appearance. It is suitable for welding with wire and strip electrodes of the chromium & chromium-nickel and chromium-nickel-molybdenum steel types either with or without niobium. Exaton 10SW is an all round flux which can be used for many applications varying from surfacing continuous caster rolls to large components in chemical plants.
Klasifikace
| Jakost | S A CS 2 Cr |
| Název | EN ISO 14174 |
Charakteristika svařovacího materiálu
| Index bazicity | nom: 1.0 |
| Hustota | nom: 1.0 kg/l |
| Typ strusky | Calcium silicate SiO2-MgO-Al2O3-(CaF2) |
| Svařovací proud | 1200 A (Using 60x0.5 mm strip) |
Spotřeba tavidla
| V | Hmotnost tavidla/1kg, drát DC |
| 26 V | 0.4 kg |
| 30 V | 0.55 kg |
| 34 V | 0.7 kg |
| 38 V | 0.9 kg |
| A | Rozměry | Rychlost přesunu |
| 580 A | 4.0 mm | 33 m/h |
Klasifikace
| Svařovací drát | AWS/EN | Po svaření |
| Exaton 19.9.Nb | A5.9:ER347/ 14343-A:S 19 9 Nb | - |
| Exaton 19.12.3.L | A5.9:ER316L/ 14343-A:S 19 12 3 L | - |
| Exaton 19.9.L | A5.9:ER308L/ 14343-A:S 19 9 L | - |
| Exaton 19.12.3.L | A5.9:EQ316L/ 14343-A:B 19 12 3 L | - |
| Exaton 19.13.4.L | A5.9:EQ317L/ 14343-A:B 19 13 4 L | - |
| Exaton 19.9.LNb | A5.9:EQ347/ 14343-A:B 19 9 Nb | - |
| Exaton 19.9.L | A5.9:EQ308L/ 14343-A:B 19 9 L | - |
| Exaton 21.13.3.L | A5.9:EQ(309LMo)/ 14343-A:B 21 13 3 L | - |
| Exaton 22.8.3.L | A5.9:EQ2209/ 14343-A:B 22 9 3 N L | - |
| Exaton 23.11.LNb | A5.9:EQ”309LNb”/ 14343-A:B 23 12 L Nb | - |
| Exaton 24.13.LNb | A5.9:EQ”309LNb”/ 14343-A:B 23 12 Nb | - |
| Exaton 24.13.L | A5.9:EQ309L/ 14343-A:B 23 12 L | - |
| Exaton 19.12.3.L | A5.9:ER316L/ 14343-A:S 19 12 3 L | A5.39: F80A10-ER316L/316L |
Schválení
| Svařovací drát | VdTÜV |
| 19.9.LNb ESW | * |
| Exaton 19.12.3.L | * |
| Exaton 19.9.L | * |
| Exaton 19.9.LNb | * |
| Exaton 19.9.Nb | * |
| Exaton 22.8.3.L | * |
| *Pouze pro vybraný výrobní závod. Pro další informace prosím kontaktujte ESAB. Navštivte stránky esab.com a stáhněte si materiálový list konkrétní kombinaci tavidlo/drát kde jsou uvedeny potřebné detaily. |
Typické mechanické vlastnosti
| Svařovací drát | Podmínky | Mez skluzu | Mez pevnosti v tahu | Zkouška rázem | Prodloužení |
| Exaton 19.12.3.L | Po svaření null | 420 MPa (61 ksi) |
580 MPa (84 ksi) |
69 J @ 20°C, (51 ft-lb @ 68 °F) 60 J @ -40°C, (44 ft-lb @ -40 °F) 55 J @ -70°C, (41 ft-lb @ -94 °F) 50 J @ -196°C, (37 ft-lb @ -320.8 °F) |
32 % |
| Exaton 19.9.L | Po svaření null | 400 MPa (58 ksi) |
580 MPa (84 ksi) |
69 J @ 20°C, (51 ft-lb @ 68 °F) 59 J @ -40°C, (44 ft-lb @ -40 °F) 40 J @ -196°C, (30 ft-lb @ -320.8 °F) |
38 % |
| Exaton 19.9.Nb | Po svaření Joining | 440 MPa (64 ksi) |
625 MPa (91 ksi) |
72 J @ 20°C, (53 ft-lb @ 68 °F) 61 J @ -40°C, (45 ft-lb @ -40 °F) 34 J @ -196°C, (25 ft-lb @ -320.8 °F) |
38 % |
Chemické složení svarového kovu
| Typického chemické složení svarového kovu v % | ||||||||||||||
| C | Cr | Cu | FN WRC-92 | Mn | Mo | N | Nb | Nb+Ta | Ni | P | S | Si | Si+Fe | |
| Exaton 19.12.3.L (Layer 1 with "24.13.L" & Layer 2 with "19.12.3.L") | ||||||||||||||
| 0.02 % | 19.0 % | - % | - | 0.8 % | 2.2 % | 0.06 % | 0 % | - | 11.5 % | - % | - % | 0.7 % | - % | |
| Exaton 19.12.3.L 2.4mm, DC+ 400A, 28V, 50 cm/min | ||||||||||||||
| 0.02 % | 18.5 % | 0.16 % | 7 % | 1.2 % | 2.4 % | 0.05 % | 0.01 % | - | 11.5 % | - % | - % | 0.65 % | - | |
| Exaton 19.13.4.L Layer 1 with "21.13.3.L" | ||||||||||||||
| <=0.04 % | 18.5 % | - % | - | - % | 3.3 % | - | - | - | 13 % | - % | - % | - % | 5 % | |
| Exaton 19.9.L 1st layer with "24.13.L" | ||||||||||||||
| <=0.03 % | 19.7 % | - % | - | - % | - % | - | - | - | 10.0 % | - % | - % | - % | 8 % | |
| Exaton 19.9.LNb ASTM 347 (Layer 1 with "24.13.LNb") | ||||||||||||||
| 0.02 % | 21.0 % | - % | - | 0.8 % | 0.0 % | 0.05 % | 0.3 % | - | 10.4 % | - % | - % | 0.6 % | - % | |
| Exaton 19.9.Nb Layer 1 with "24.13.LHF" & 2 layers with "19.9.Nb" | ||||||||||||||
| 0.04 % | 19.0 % | 0.1 % | - | 0.6 % | 0.01 % | 0.06 % | 0.3 % | 0.3 % | 9.2 % | 0.01 % | 0.01 % | 1.0 % | - | |
| Exaton 22.8.3.L Layer 1 with "24.13.L" & 2 layers with "22.8.3.L" | ||||||||||||||
| <=0.03 % | 22.7 % | - | - | - % | 2.9 % | 0.16 % | - | - | 8.5 % | - % | - % | - % | 40 % | |
| Exaton 23.11.LNb | ||||||||||||||
| <=0.06 % | 19 % | - % | - | - % | - % | - | - % | - | 9.7 % | - % | - % | - % | 7 % | |
| Exaton 24.13.L Layer 1 with "24.13.L" | ||||||||||||||
| <=0.07 % | 19.2 % | - % | - | - % | - % | - | - | - | 10.5 % | - % | - % | - % | 6 % | |
| Exaton 24.13.LNb | ||||||||||||||
| <=0.06 % | 19.2 % | - % | - | - % | - % | - | - % | - | 9.7 % | - % | - % | - % | 6 % | |