SHIELD-BRIGHT 308H

SHIELD-BRIGHT 308H

Shield-Bright 308H was developed for welding Type 304H stainless steel and can also be used for welding Type 301, 302, and 304 steels. It contains a higher carbon level than 308L filler metals to give greater high temperature strength. The ferrite content is also lower for high temperature service. It has greater ductility than 347 types at high temperatures and for that reason it is sometimes used to weld Types 321 and 347 for service above 750°F (399°C) coupled with high stress.

Add to shopping list


Industries

  • Industrial and General Fabrication
  • Petrochemical
  • Power Generation

Welding Process

  • Welding-FCAW - Flux Core Arc Welding

Specifications


Typical Tensile Properties

M21 Shielding Gas As welded
Elongation Tensile Strength Yield Strength
46 % 84 ksi 54 ksi

Typical Charpy V-Notch Properties

C1 Shielding Gas As welded
Impact Value Testing Temperature
47 J -29 °C
26 J -196 °C

Typical Weld Metal Analysis %

75% Ar - 25% CO2
MnCSiNiCr
1.08 %0.05 %0.87 %9.65 %19.21 %

Classifications: SFA/AWS A5.22, E308HT1-1, Weld Metal, SFA/AWS A5.22, E308HT1-4, Weld Metal, JIS Z 3323, YF 308C, Weld Metal, KS D 3612, YF 308C, Weld Metal, EN ISO 17633-A, T 19 9 H P M21 2, Weld Metal, JIS Z 3232, TS308H-FB1, Weld Metal, EN ISO 17633-A, T 19 9 H P C1 2

Alloy Type: C Cr Ni
Welding Current: DC+