ATOM ARC 7018

Inquire about this product
ATOM ARC 7018

Documents


Typical Tensile Properties

Condition Elongation Reduction in Area Stress Relieved Temperature Stress Relieved Testing Time Tensile Strength Yield Strength
Stress Relieved 33 % 77 % 1150 °F 8 hr 70 ksi 57 ksi
As Welded 30 % 75 % - - 78 ksi 68 ksi

Typical Charpy V-Notch Properties

Condition Impact Value Testing Temperature Stress Relieved Testing Temp Stress Relieved Testing Time
As Welded 168 ft-lb -20 °F - -
Stress Relieved 193 ft-lb -20 °F 1150 °F 8 hr

Typical Weld Metal Analysis %

ELEMENTVALUES
PMnCSSi
0.015 %1.10 %0.045 %0.014 %0.40 %

Deposition Data

Diameter Current Deposition Rate Efficiency (%) Optimal Amps
5/32 in.
4.0 mm		 130-220 A 3.8 lb/h
1.7 kg/h 		73.5 % 170 A
1/4 in.
6.4 mm		 300-400 A 7.7 lb/h
3.5 kg/h 		78 % 300 A
1/4 in.
6.4 mm		 300-400 A 8.7 lb/h
3.9 kg/h 		77 % 350 A
3/16 in.
4.8 mm		 200-300 A 4.9 lb/h
2.2 kg/h 		76.4 % 200 A
3/16 in.
4.8 mm		 200-300 A 5.4 lb/h
2.4 kg/h 		74.6 % 250 A
3/32 in.
2.4 mm		 70-100 A 1.7 lb/h
0.8 kg/h 		66.3 % 90 A
7/32 in.
5.6 mm		 250-350 A 6.5 lb/h
2.9 kg/h 		75 % 250 A
7/32 in.
5.6 mm		 250-350 A 7.2 lb/h
3.3 kg/h 		74 % 300 A
1/8 in.
3.2 mm		 90-160 A 2.6 lb/h
1.2 kg/h 		71.6 % 120 A
1/8 in.
3.2 mm		 90-160 A 2.7 lb/h
1.2 kg/h 		70.9 % 140 A
5/32 in.
4.0 mm		 130-220 A 3.1 lb/h
1.4 kg/h 		75 % 140 A

Approvals: ABS; 2Y/AWS A5.1: E7018; CWB CSA W48; E4918; DNV; 3Y(H10); LR; 3m,3Ym(H10); MIL-E-22200/1; MIL-7018
Classifications: ASME SFA 5.1; AWS A5.1; E7018 H4R

Approvals are based on factory location. Please contact ESAB for more information.


x
×

Find the Closest Distributor

Mechanized Cutting customer? Click here.

x

Find the Closest Distributor

Mechanized Cutting customer? Click here.

x

x

Loading..