5
All-State Fluxes and Fluxing Systems
Suggested Active
Type
and Product
Filler Metal TemperatureRange
Specifications 1113
For welding and brazing at high temperature
on cast iron, mild steel, 11,
13 1400°F
to 2200°F AWS A5.31
nickel
silvers and copper — remains protective at 2200°F (12040C).
Type
FB3-G DUZALL
For soldering — a general purpose flux
for use with all soft solders All
Steels 430°F
Fed AA51145
on
stainless,copper base alloys, gold, silver and galvanized steel.
Copper Alloys
Type 1, Form B
DUZALL NCR PASTE
A white to yellowish paste flux formulated
for copper based metals, Copper
Alloys 2500F
to 5200F
clean carbon
steels, new galvanized steel, silver, gold, and tinplate. Carbon
Steels, The
flux promotes excellent wetting of solder to surfaces to be joined.
Galvanized Steels, The
little amount of residue it leaves is non-corrosive, highly water
Silver, Gold, Tinplate
soluble
and easy to remove. JET
FLUX For welding and
brazing-designed for application through the Cast
Iron, LFB, Steel 14000F-18000F
Mil-F-16135B
All-State
Jet Fluxer. Provides high temperature fluxing at the and
Copper Base flame
control point. Can be used on cast iron, steel and copper Alloys
base
metals. Ideal for production brazing fillet joints such as
furniture,
bicycles, etc. NOTE: All flux
residues should be removed by using hot water [140°F (60°C)], live steam,
wire brushing and/or chipping.